OXYDATION D'ALLIAGES FE-CR-AL. INFLUENCE DE QUELQUES FACTEURS SUR LA STRUCTURE ET LA MORPHOLOGIE DES COUCHES FORMEES
Author | : MOHAMED.. BOUALAM |
Publisher | : |
Total Pages | : |
Release | : 1992 |
ISBN-10 | : OCLC:490443718 |
ISBN-13 | : |
Rating | : 4/5 (18 Downloads) |
Book excerpt: LE BUT DE CE TRAVAIL EST L'ETUDE DE L'INFLUENCE DE QUELQUES FACTEURS SUR LA MORPHOLOGIE ET LA STRUCTURE DES COUCHES D'OXYDES OBTENUES A HAUTE TEMPERATURE SUR DES ALLIAGES FE-CR-AL, AINSI QUE SUR LEUR CINETIQUE DE CROISSANCE. NOUS AVONS PRIS EN COMPTE UN MAXIMUM DE FACTEURS D'INFLUENCE: L'ETAT PHYSICO-CHIMIQUE ET GEOMETRIQUE DE LA SURFACE, LA COMPOSITION DE L'ALLIAGE, LE TEMPS, LA TEMPERATURE ET L'ATMOSPHERE D'OXYDATION. IL A ETE CONSTATE QU'UNE COUCHE D'ALUMINE SOUS FORME DE WHISKERS EST OBTENUE AISEMENT SUR DES ALLIAGES SOUS FORME FEUILLARDS A 5% D'ALUMINIUM (GILPHAL 135 CE) LORSQUE L'OXYDATION A LIEU A 900C PENDANT 24 HEURES DANS L'AIR AMBIANT. CETTE COUCHE A ETE IDENTIFIEE COMME ETANT DE L'ALUMINE DE TRANSITION (THETA); L'EVOLUTION DE CE TYPE D'OXYDE VERS L'ALUMINE ALPHA EN FONCTION DES CONDITIONS D'OXYDATION INDUIT LA TRANSFORMATION DES WHISKERS EN PETITS CRISTAUX. AINSI IL EXISTE UNE ETROITE RELATION ENTRE LA STRUCTURE ET LA MORPHOLOGIE DES COUCHES. PAR AILLEURS, NOUS AVONS CONSTATE QUE LA TRANSITION S'OPERE POUR DES DUREES D'AUTANT PLUS COURTES QUE LA TEMPERATURE EST ELEVEE: AU-DELA DE 24 HEURES A 900C, MOINS D'UNE HEURE A 1000C. LA CROISSANCE DES WHISKERS EST LIEE A LA PRESENCE D'UNE FINE COUCHE D'ALUMINE DE TRANSITION PREEXISTANTE SUR L'ALLIAGE ET QUI RESULTE DE L'OPERATION DE RECUIT REALISEE AU COURS DE L'ELABORATION. LA VAPEUR D'EAU DANS L'ATMOSPHERE, A 900C, ACCELERE L'OXYDATION MAIS A FORTE TENEUR, FAVORISE LA TRANSFORMATION THETAALPHA. SUR LES ALLIAGES A 2% D'ALUMINIUM, LA VAPEUR D'EAU ENTRAINE LA FORMATION D'OXYDE DE FER SUR LES BORDS DES ECHANTILLONS ET DONC UNE CORROSION CATASTROPHIQUE DE CE TYPE D'ALLIAGES SE PRODUIT