ETUDE SPECTROMETRIQUE DES PREMIERS STADES DE L'OXYDATION DE L'ACIER AISI 304 A HAUTE TEMPERATURE
Author | : René Guillamet |
Publisher | : |
Total Pages | : |
Release | : 1993 |
ISBN-10 | : OCLC:490454814 |
ISBN-13 | : |
Rating | : 4/5 (14 Downloads) |
Book excerpt: NOUS AVONS OXYDE A L'AIR 900, 1000 ET 1100#OC, PENDANT 1, 5, 15 OU 60 MINUTES, DES ECHANTILLONS, POLIS MECANIQUEMENT (PATE DIAMENTEE GRADE 3 MICRONS) OU DECAPES DANS UN MELANGE HCL/HNO#3, D'ACIER INOXYDABLE AUSTENITIQUE AISI 304 18% DE CR, 10% E NI, ENVIRON 2% DE MN): LES OXYDES DEVELOPPES ONT ETE ANALYSES PAR XRD, CEMS, SPECTROSCOPIE DE REFLECTANE (IRFT ET UV-VISIBLE-PIR), SIMS ET MEB. L'OXYDATION D'ECHANTILLONS POLIS COMMENCE PAR L'APPARITION D'UNE COUCHE D'OXYDES DE CHROME (CR#2O#3 ET SPINELLE MNCR#2O#4), SUIVIE PAR LE DEVELOPPEMENT D'OXYDES DE FER. L'OXYDATION D'ECHANTILLONS DECAPES CHIMIQUEMENT CONSISTE UNIQUEMENT EN LA MONTEE D'OXYDES DE FER (ALPHA-FE#2O#3 ET PETITES PARTICULES SUPER PARAMAGNETIQUES DE ALPHA-FE#2O#3 ET UNE MAGNETITE PARTIELLEMENT SUBSTITUEE AU CR-NI). L'OXYDATION PROVOQUE UN APPAUVRISSEMENT EN CR (EN MN) DU SUBSTRAT METALLIQUE ET UNE TRANSFORMATION DE PHASE GAMME (C.F.C.)ALPHA (C.C.) DANS LA MATRICE (PRES DE L'INTERFACE OXYDES-METAL)