Block Copolymer Thin Films for Nanometer Pattern Generation and Nanostructure Synthesis
Author | : Hai Wang |
Publisher | : Open Dissertation Press |
Total Pages | : |
Release | : 2017-01-27 |
ISBN-10 | : 1374666580 |
ISBN-13 | : 9781374666580 |
Rating | : 4/5 (80 Downloads) |
Book excerpt: This dissertation, "Block Copolymer Thin Films for Nanometer Pattern Generation and Nanostructure Synthesis" by Hai, Wang, 王海, was obtained from The University of Hong Kong (Pokfulam, Hong Kong) and is being sold pursuant to Creative Commons: Attribution 3.0 Hong Kong License. The content of this dissertation has not been altered in any way. We have altered the formatting in order to facilitate the ease of printing and reading of the dissertation. All rights not granted by the above license are retained by the author. Abstract: Abstract of thesis entitled BLOCK COPOLYMER THIN FILMS FOR NANOMETER PATTERN GENERATION AND NANOSTRUCTURE SYNTHESIS submitted by HAI WANG for the Degree of Doctor of Philosophy at The University of Hong Kong in August 2006 Block copolymers show great potential in nanofabrication, therefore, studies of self assembly in block copolymers and their application for nanostructure synthesis are of considerable interest. The self assembly of asymmetric di- block copolymer poly(styrene ethylene oxide) and poly(styrene-block-methyl methacrylate)thin...lmsisstudiedinthisthesisandtheapplicationofpoly(styrene ethyleneoxide) as astructuredirectingagent inthe synthesis of mesoporous ti- tania structure is also investigated. Firstly, factors aecting the self assembly were systemically examined for thin ...lms of two asymmetric diblock copolymers: poly(styrene-block-methyl methacrylate)(P(S-b-MMA))andpoly(styreneethyleneoxide)(P(S-b-EO)).ItwasfoundthatthemorphologyofP(S-b-MMA)isstronglythicknessdependent. Five representative morphologies are identi...ed. Contrary to generally-accepted concept, themorphologywithperpendicularPMMAcylindersinPSmatrixwas obtained for the ...lm thickness range of 48 nm to 63 nm on SiOx/Si substrates withoutapplyingexternalelectric...eldoranysurfacetreatment(hydrogenpas- sivation, functionalizedrandomcopolymers, orself-assembledmonolayers). The ...lms with uniform ordering at large scale can be obtained after annealing by choosing the proper spinning speed, solution concentration, substrate cleaning procedure, and annealing conditions. On the other hand, P(S-b-EO) thin ...lms donotexhibitthicknessdependenceofthemorphology. Perpendicularcylinders were obtained in all cases. Therefore, P(S-b-EO) has been chosen as a model system for comprehensive studies of factors aecting phase contrast in tapping modeatomicforcemicroscopy. Thecorrelationbetweenthephasecontrastand the elasticity of PEO domains and PS matrix in the poly(styrene ethylene ox- ide) thin ...lmwas established and explained with the energy dissipation theory. The phase contrast was also found to be dependent on the atomic force mi- croscope used due to dierent methods of detecting phase contrast in dierent microscopes. After detailed characterization of P(S-b-EO), this diblock copolymer was used as the structure directing agent for the synthesis of mesoporous titania nanostructures. The developed method for titania synthesis is simple and highly reproducible. The morphologies of the mesoporous titania structures can be controlled by titania precursor concentration, diblock copolymer P(S- b-EO), solvents and annealing conditions. The thermally stable mesoporous titania structure was used in heterojunction solar cells with device structure ITO/Titania/MEH-PPV/Au. The short circuit current densities of the solarcellswereimprovedoverthepreviousreports, whichcanbeattributedtobetter conjugatedpolymer...llingandincreasedchargecarrierpercolationpathsinthe bicontinuous titania mesostructure with large pore size. DOI: 10.5353/th_b3697984 Subjects: Copolymers Thin films Nanostructured materials - Synthesis