ETUDE PAR ABSORPTION X DE MATERIAUX CERAMIQUES OBTENUS PAR PYROLYSE DE PRECURSEURS ORGANOSILICIES
Author | : CARINE.. LAFFON |
Publisher | : |
Total Pages | : |
Release | : 1990 |
ISBN-10 | : OCLC:490263909 |
ISBN-13 | : |
Rating | : 4/5 (09 Downloads) |
Book excerpt: CE TRAVAIL EST CONSACRE A L'ETUDE PAR SPECTROSCOPIE D'ABSORPTION X AU SEUIL K DU SILICIUM DES FIBRES LONGUES DE TYPE SIC ET SICN. CES CERAMIQUES PAR LEURS QUALITES THERMOMECANIQUES, SONT DESTINEES A LA FABRICATION DE MATERIAUX COMPOSITES POUR DES APPLICATIONS A HAUTES TEMPERATURES. LE CONCEPT D'ELABORATION DE LA CERAMIQUE A PARTIR D'UN POLYMERE PRECURSEUR ORGANOMETALLIQUE ET LES METHODES DE FABRICATION DEMANDENT DES OPTIMISATIONS. L'EXAFS A PERMIS DE DECRIRE L'ENVIRONNEMENT STRUCTURAL DU SILICIUM DANS DEUX TYPES DE FIBRES SIC COMMERCIALISEES PAR NIPPON CARBON. LE MODELE PROPOSE DECRIT CES MATERIAUX COMME ETANT CONSTITUES DE CRISTAUX NANOMETRIQUES JOINTS ENTRE EUX PAR UNE PHASE SIC#XO#Y. EN COLLABORATION AVEC LE LABORATOIRE DES COMPOSITES THERMOSTRUCTURAUX DE BORDEAUX, NOUS AVONS ETUDIE LE MATERIAU EN COURS D'ELABORATION: LE PRECURSEUR DE LA FIBRE COMMERCIALE PREFIGURE LA STRUCTURE SIC QUI SE DEVELOPPERA AU COURS DE LA PYROLYSE. MAIS LES CONDITIONS DE PYROLYSE MODIFIENT LA STRUCTURE DES MATERIAUX OBTENUS: ILS PRESENTENT UNE HETEROGENEITE DE TAILLE DE CRISTAUX SIC AINSI QUE DES DIFFERENCES DE TENEUR EN OXYGENE EN COMPARAISON AVEC LA FIBRE COMMERCIALE. LE ROLE DE L'OXYGENE SUR LA CROISSANCE DES CRISTALLITES SIC A ETE MIS EN EVIDENCE. POUR ETUDIER L'INFLUENCE DES CONDITIONS INITIALES, D'AUTRES ETUDES CONCERNENT LA CERAMISATION D'UN PRECURSEUR CONTENANT DES LIAISONS SI-N. NOUS RENDONS COMPTE DE MANIERE ANALOGUE AU MATERIAU COMMERCIAL D'UNE STRUCTURE A DOMINANTE DE CRISTAUX JOINTS ENTRE EUX PAR UN SYSTEME DE LIAISONS MIXTES PLUS SOUPLE DE PHASE SILICO-AZOTEE. LE XANES MONTRE DES SIGNATURES TRES NETTES D'UN TYPE D'ENVIRONNEMENT. EN S'APPUYANT SUR LES RESULTATS OBTENUS PAR EXAFS, NOUS AVONS CORRELE LES VARIATIONS DE STRUCTURES FINES DU SEUIL AVEC LES DONNEES D'EVOLUTION STRUCTURALE DU MATERIAU