COMPORTEMENT A L'OXYDATION DE CERAMIQUES A BASE DE NITRURE DE SILICIUM EN ATMOSPHERE COMPLEXE AIR/SO#2
Author | : JEAN-BERNARD.. VEYRET |
Publisher | : |
Total Pages | : |
Release | : 1989 |
ISBN-10 | : OCLC:799260610 |
ISBN-13 | : |
Rating | : 4/5 (10 Downloads) |
Book excerpt: L'ETUDE DE L'INFLUENCE DE LA MICROSTRUCTURE DE NITRURES DE SILICIUM FRITTES SUR LES LOIS DE COMPORTEMENT DANS L'AIR CHARGE DE GAZ SULFUREUX A HAUTE TEMPERATURE A PERMIS DE PRECISER DANS UN PREMIER TEMPS LEUR RESISTANCE A L'OXYDATION EN ATMOSPHERE EXEMPTE DE SOUFRE. ON PEUT DISTINGUER DEUX GRANDS TYPES DE MATERIAUX, CEUX COMPORTANT DES PHASES VITREUSES RESIDUELLES RESULTANT DE L'EMPLOI D'AJOUTS ALCALINO-TERREUX ET CEUX BEAUCOUP PLUS RARES, PRESENTANT DES PHASES SECONDAIRES CRISTALLINES PRECIPITANT AISEMENT; C'EST LE CAS DE L'YTTRIUM UTILISE COMME AJOUT DE FRITTAGE. UNE ATMOSPHERE COMPLEXE AIR-SO#2 NE MODIFIE PAS LES MECANISMES D'OXYDATION, NI LE COMPORTEMENT MECANIQUE A HAUTE TEMPERATURE. L'INFLUENCE DU SOUFRE EN ATMOSPHERE OXYDANTE N'EST DONC PAS A CRAINDRE; ELLE PEUT MEME ETRE BENEFIQUE DANS CERTAINS CAS OU INTERVIENT L'YTTRIUM SI LES SULFATES FORMES A PARTIR D'IMPURETES MINEURES, TELLES LE CALCIUM OU LE SODIUM PERMETTENT UNE MEILLEURE STABILITE DU REVETEMENT PROTECTEUR FORME AU COURS DE L'OXYDATION